Phenolic Moulding Compound
(High temperature resistant for skeleton material, Grade: PF2D1-161J)
Phenolic Moulding Compound
RuiDa’s Phenolic Moulding Material (Bakelite Powder) are combined with phenolic formaldehyde resin, wood flour, hexamine, pigment and other materials.
PF2D1-161J: injection grade; color: black, red, brown
l Product Properties
1. Filled high temperature endured mineral materials and fire retardant,
2. With best flammability and hot tin(Sn) endurance performance
3. UL listed molding compound, 3.0 mm / V-0 (ALL).
l Applications
Used for making coil structure framework, electrical insulated components.
l Production Specification
Q/ZWS.C10.1B-2002 | ||||||
Workshop | PMC First Line | Report Number | / | |||
Porduct Name | Bakelite Powder | Production Date | / | |||
Model | PF2D1-161J | Report Date | / | |||
Color | Black | Technical Standard | GB1404.3-2008 | |||
Number | Test Items | Index | Test Result | |||
1 | Fluidity, mm | 100-130 | 125 | |||
2 | Volatile Content % ≤ | 4.00 | 2.2 | |||
3 | Apparent Density g/ml | / | 0.75 | |||
4 | Specific Gravity g/cm3 | / | 1.456 | |||
5 | Volume Resistivity MΩ*cm | ≥1011 | 1.7×1013 | |||
6 | Surface Resistivity Ω | ≥1010 | 2.7*1012 | |||
7 | Flexural Strength, Mpa ≥ | 80 | 100 | |||
8 | Impact Strength(with notch), KJ/㎡ ≥ | 1.5 | 1.85 | |||
9 | Temperature of hot distortion, ℃ ≥ | 160 | 220 | |||
10 | Water absorption(Cold water) mg ≤ | 100 | 50 | |||
11 | Molding Shrinkage, % | 0.5-0.8 | 0.76 | |||
12 | Dielectric Strength, KV/mm ≥ | 10 | 15 | |||
13 | Thermal Expansion(Tin dipping), mm ≤ | 0.5 | 0.26 | |||
14 | Comparative Tracking Index ( PTI ), V ≥ | 125 | 150 | |||
15 | Flammability (heat rod) BH V | ≤BH2-10 | BH2-10 | |||
Note | This product can be stored for 12 months under a temperature less than 35℃. This product tends to absorbing moisture, so place it in a cool and dry place under a temperature less than 35℃ and use it up as soon as possible within 12 months. While taking it out of the bag, take care to avoid dampness and dust. | |||||
l Injection Molding Condition
Mould temp.℃ | Cylinder temp.℃ | Injection pressure MPa | Mold closing pressure MPa | Back pressure MPa | Time s/mm | ||
Fixed mould | Moving mould | Front | Back | ||||
165-175 | 170-180 | 90-100 | 70-80 | 80-160 | 100-200 | 1-3 | 10-20 |
l Additional information:
1x20GP can load 21 tons, 840 bags, without pallet.
Delivery period: within 7 days.
Packaging: PP/ Kraft bag with wet proof inner bag. 25kgs/bag
Storage period: 1 year kept in cool warehouse.